Structural development in molecular semiconductors for thin-film electronics

发布时间:2018-03-07

点击量:

Speaper:  Yueh-Lin (Lynn) Loo 
Date:   March 8, 2018
Time:  10:30-12:00 a.m.
Venue:  C125

Abstract:
Though both the molecular orientation and crystal structure of molecular semiconductors are known to impact charge transport in thin-film devices, controllably accessing different polymorphs and tuning both the in-plane and out-of-plane molecular orientations remain challenging, requiring careful selection of film deposition conditions, film thickness, and substrate chemistry. Without necessitating any specification of these parameters, we have been able to impose specific polymorphs and/or preferential molecular orientation by decoupling film formation from structural development and controlling the latter through post-deposition processing.  
In the case of contorted hexabenzocoronene (HBC), we can access two distinct polymorphs and independently vary the distributions of its out-of-plane molecular orientation.  Starting with a thermally evaporated amorphous HBC film, thermal and solvent-vapor annealing induces the thin film to crystallize into distinct polymorphs; we can further transform between the polymorphs with subsequent rounds of processing.  Because the molecular orientation distribution is primarily determined during the first processing step, subjecting already crystalline thin films to different post-deposition processing conditions allows us to access different polymorphs without altering the molecular orientation distribution, thus enabling us to decouple the influence of each on charge transport.       
In the case of solution-processable triethylsilylethnyl anthradithiophene (TES ADT), we have been able to exploit its differential crystallization rates on substrates having different surface energies to guide the in-plane growth direction of neighboring crystals.  The systematic engineering of solely low- and high-angle grain boundaries between neighboring crystals have allowed us to elucidate their relative contribution to charge transport.
 
Introduction:
Lynn is a fellow of the American Physical Society, and received its John H. Dillon Medal. A Young Global Leader of the World Economic Forum, she has also been recognized by Sloan and Beckman Fellowships, the Peterand Edith O’Donnell Award in Engineering from the Texas Academy of Medicine, Science and Engineering, and the Alan P. Colburn Award from the American Institute of Chemical Engineers for her scholarship.
 

 

深圳市南山区桃园街道南山智园二期D2栋4楼409室

Copyright © 2011 登录云顶集团-云顶集团游戏登录网站【首頁】 Powered By its.pkusz.edu.cn

ICP备案编号:粤ICP备

  • 学院官方微信